The Low E glass coating layer adopts high temperature chemical vapor deposition (CVD), which is integrated with the glass after annealing and cooling. It has good chemical and mechanical stability. At the same time, the transmittance, conductivity and haze of the product are perfect. Optimized balance. It can be widely used in commercial and civil building indoor and outdoor decoration, household appliances and other fields.
In winter, Low E glass can reflect heat back into the room to prevent heat loss and help maintain a uniform indoor temperature. In summer, Low E glass can reduce the amount of heat entering the room to make the room cooler and more comfortable.
2.Low E glass technical indicators
Low E Insulated Glass Performance(the coating is on the second side)
3.Low E glass product advantages
1-Using advanced CVD coating technology, the coating is directly carried out during the glass production process, and the film layer and the glass are combined as a whole
2- It can be used for glass doors, windows and curtain walls on all commercial and civil buildings, with soft colors and no color difference
3-The film is stable, durable, and can be exposed to the air for a long time, which is convenient for storage and transportation
4- It can be used as a single piece or made into insulating glass or laminated glass
5-Easy for secondary processing and processing such as hot bending, tempering and semi-tempering
6-Flexible size, short lead time
7-Lower cost, better price
4.Low E glass product specifications
Thickness:3.2mm, 4mm, 5mm, 6mm, 8mm, 10mm and 12mm etc.
Size and deep processing: The standard size range is 2140mm×3300mm, 2440mm×3300mm and 5100mm×3300mm; it can be customized according to customer needs.
The Low E glass coating layer adopts high temperature chemical vapor deposition (CVD), which is integrated with the glass after annealing and cooling. It has good chemical and mechanical stability. At the same time, the transmittance, conductivity and haze of the product are perfect. Optimized balance. It can be widely used in commercial and civil building indoor and outdoor decoration, household appliances and other fields.
In winter, Low E glass can reflect heat back into the room to prevent heat loss and help maintain a uniform indoor temperature. In summer, Low E glass can reduce the amount of heat entering the room to make the room cooler and more comfortable.
2.Low E glass technical indicators
Single panel Low E glass performance
Clear Low E Glass
Low Iron Low E Glass
Clear Low E Glass
Épaisseur | Lumière visible | Solaire | Valeur U | g | Sc | ||||
mm | Trans. % | Réf.% | Trans.% | Réf.% | Hiver | Été | |||
dehors | dans | ||||||||
4 | 83 | 10 | 11 | 71 | 11 | 3.6 | 2.7 | 0.74 | 0.85 |
5 | 82.5 | 11 | 12 | 68 | 12 | 3.6 | 2.7 | 0.72 | 0.82 |
6 | 82 | 11 | 12 | 68 | 11.5 | 3.55 | 2.7 | 0.71 | 0.81 |
8 | 81 | 11.7 | 12.8 | 64 | 11.5 | 3.5 | 2.65 | 0.68 | 0.78 |
Low Iron Low E Glass
Épaisseur | Lumière visible | Solaire | Valeur U | g | Sc | ||||
mm | Trans. % | Réf.% | Trans.% | Réf.% | Hiver | Été | |||
dehors | dans | ||||||||
4 | 84 | 12.9 | 13.5 | 74.9 | 13.6 | 3.6 | 2.7 | 0.77 | 0.88 |
5 | 84 | 13.2 | 13.5 | 74.7 | 13.7 | 3.6 | 2.7 | 0.77 | 0.88 |
6 | 83.5 | 13.5 | 13.5 | 74.6 | 13.7 | 3.6 | 2.7 | 0.77 | 0.88 |
8 | 83 | 14 | 14 | 74 | 14 | 3.5 | 2.65 | 0.76 | 0.88 |
Low E Insulated Glass Performance(the coating is on the second side)
Verre isolant | Lumière visible | Solaire | Valeur U | g | Sc | ||||
Trans. % | Réf.% | Trans.% | Réf.% | Hiver | Été | ||||
dehors | dans | ||||||||
4mm clair low-e + 12A + 4mm clair | 75 | 17.5 | 16 | 60 | 15 | 1.9 | 1.9 | 0.72 | 0.83 |
5mm clair low-e + 12A + 5mm clair | 74 | 18 | 17 | 57 | 16 | 1.9 | 1.9 | 0.70 | 0.81 |
6mm clair low-e + 12A + 6mm clair | 74 | 18 | 17 | 54 | 16 | 1.8 | 1.8 | 0.67 | 0.77 |
8mm clair low-e + 12A + 8mm clair | 72 | 18.5 | 17 | 48 | 15 | 1.8 | 1.8 | 0.62 | 0.71 |
6mm faible fer + 12A + 6mm faible fer | 83.4 | 18 | 18 | 79 | 17 | 2.5 | 2.5 | 0.8 | 0.9 |
6mm faible fer low-e + 12A + 6mm low iron | 77 | 20 | 21 | 67 | 20 | 1.6 | 1.6 | 0.7 | 0.8 |
3.Low E glass product advantages
1-Using advanced CVD coating technology, the coating is directly carried out during the glass production process, and the film layer and the glass are combined as a whole
2- It can be used for glass doors, windows and curtain walls on all commercial and civil buildings, with soft colors and no color difference
3-The film is stable, durable, and can be exposed to the air for a long time, which is convenient for storage and transportation
4- It can be used as a single piece or made into insulating glass or laminated glass
5-Easy for secondary processing and processing such as hot bending, tempering and semi-tempering
6-Flexible size, short lead time
7-Lower cost, better price
4.Low E glass product specifications
Thickness:3.2mm, 4mm, 5mm, 6mm, 8mm, 10mm and 12mm etc.
Size and deep processing: The standard size range is 2140mm×3300mm, 2440mm×3300mm and 5100mm×3300mm; it can be customized according to customer needs.